The phenomenon of steering wheel shaft head fracture in use of forklift truck is a simple maintenance method.​

The phenomenon of steering wheel shaft head fracture in use of forklift truck is a simple maintenance method.​

It is recommended to refer to the heavy machinery service manual for forklift maintenance methods.​

1. Finish the welding parts according to the technical requirements of the parts, and pay attention to the tolerance of the bearing fitting part. The welding seam st

The phenomenon of steering wheel shaft head fracture in use of forklift truck is a simple maintenance method.​

rength can meet the use requirements according to the experience calculation. The repaired shaft head has been used for more than one year and everything is normal.

 

2. Welding steering wheel shaft and shaft head accessories. 607 welding rod is selected (ensure that the strength of the weld is equal to that of the mother village), the drying temperature before welding is 350-450℃, with the heating of the furnace, the heat preservation is 1-2h, with the use of as the take; ​preheat the base metal to about 250℃; ​use DC welder with small current welding, after each welding layer with a small hammer on the section of the weld, in order to eliminate internal stress; ​at the same time, after observing that there is no crack in the welding part, the next layer can be welded to ensure the welding quality.

3. The shaft head fittings shown in the forklift shall be made of 45# steel, and the round boss shall be pressed into the countersunk hole of the original shaft head, and the fit relation shall be H7/ S6.

4. On the lathe, the shaft head fracture end is turned off, and boring a countersunk hole with a diameter of φ35mm and a depth of 15mm on the section, and then open a chamfer of 10×60° on the outer circle. By calculation, the bending moment M=1410N· M and tensile force S=7030N of this section are not large, but the cross-sectional area is large, so the cross-sectional force is small.